<p>As @T. M. notes in his comment, there are many good charts of chemical compatibility with various agents.  Very few (I found none) include information about PLA.  By all means, use search engines to find some information.</p>

<p>But, no data source is as true to your specific needs as is testing your candidate materials with your agents.  </p>

<p>As a first test put the agent in a tall thin jar or test tube.  Use a few test filaments so that the ends are dipping into the agent.  Check for signs of dissolution, swelling, softening, or any relevant change in the material's characteristics.  Examine the candidate filaments right away, then after minutes, then hours, and if any material survives, perhaps in days.</p>

<p>Print test objects.  Test them with your agent.  Try until you find something that works.</p>

<p>The online material compatibility tables will help you eliminate materials before testing them.  If it says a material is incompatible, it probably is incompatible.  If rated as highly compatible, it should be tested because the formulation of a filament may not match the material tested for the compatibility tables.  If you are running out of options, try the intermediate compatibility plastics.</p>

<p>Bottom line, use the online information to help direct your search, but you should do your own tests.</p>

CC BY-SA 4.0
2019-07-22T18:51:34.447Z
2019-07-22T18:51:34.447Z
cmm
<p>See this as well:</p>
<p><a href="https://www.filamentive.com/chemical-resistance-of-3d-printing-filament/" rel="nofollow noreferrer">Chemical Resistance of 3D Printing Filament</a> by Ravi Toor</p>
<blockquote>
<p>Summarised chemical resistance per material below (<em><strong>H</strong>= High Resistance, <strong>VH</strong> = Very High Resistance</em>).</p>
<p><strong>Water</strong> – PLA (H) PETg (VH), CF-PETg (VH), ASA (VH), ABS (VH), ePLA (H), ONE PET (H)</p>
<p><strong>Acids</strong> – PETg (VH), ASA (VH), ABS (H)</p>
<p><strong>Bases</strong>– PETg (VH), CF-PETG (VH), ASA (VH)</p>
<p><strong>Alcohols</strong> –PETg (H), CF-PETG (VH), ASA (VH), ABS (H)</p>
<p><strong>Hydrocarbons</strong> – N/A</p>
<p><strong>Ketones</strong> –N/A</p>
<p><strong>Ethers</strong> –N/A</p>
<p><strong>Fuels</strong> –PETg (H), CF-PETG (H)</p>
<p><strong>Salts</strong> – PLA (H), ASA (VH), ABS (VH), ePLA (H)</p>
<p><strong>UV</strong> –PLA (H), ASA (VH), ABS (H), ePLA (H)</p>
<p><strong>Oils</strong> – PLA (H), PETg (VH), CF-PETg (VH), ASA (H), ePLA (H)</p>
</blockquote>

CC BY-SA 4.0
2022-01-19T20:35:29.563Z
Welcome to 3D Printing SE and thank you for your contribution. When you get a chance, please take the [tour] to understand how the site works and how it is different than others.
agarza
CC BY-SA 4.0
2022-01-19T20:11:08.507Z
2022-01-20T05:03:03.823Z
2022-01-20T05:03:03.823Z
Guggolo
<p>The paper <a href="https://www.researchgate.net/publication/326697946_Chemical_Compatibility_of_Fused_Filament_Fabrication-based_3-D_Printed_Components_with_Solutions_Commonly_Used_in_Semiconductor_Wet_Processing" rel="nofollow noreferrer">Chemical Compatibility of Fused Filament Fabrication-based 3-D Printed Components with Solutions Commonly Used in Semiconductor Wet Processing</a>, found by user R Kiselev in the comments on <a href="https://3dprinting.stackexchange.com/questions/13897/how-to-get-a-quality-print-of-a-thin-single-walled-shell">another question</a>, has results for this, and finds (this is summarized; details in paper) that PLA has fairly good resistance to HCl at 37%. It did not fare as well against other acids or solvents except IPA.</p>

CC BY-SA 4.0
2020-06-17T22:45:49.597Z
2020-06-17T22:45:49.597Z
R.. GitHub STOP HELPING ICE
<p>I'm interested in 3d printed reaction chambers, but can't find any good information on chemical resistances of PLA, just vague claims that it "might not be" "because it's biodegradable" or that it depends on additives (likely true, but it would be nice to know if there's hope of finding PLA without problematic additives if the PLA itself is okay). Is there any published research or even anecdotes (which could suggest it's worth spending effort to investigate further) on this topic?</p>

CC BY-SA 4.0
2019-04-11T17:55:37.323Z
You could test HCl resistance by squirting out some clorox into a small glass and dip a failed print in. Other acids may be hard to come by using common household chemicals.
Lux Claridge
CC BY-SA 4.0
2019-04-11T19:13:07.267Z
actually, this calls for a lab test... I would suggest to design some kind of sample piece (like, a small tray with a diameter 2mm cylindrical cavity, 1.5mm material to the sides, 1mm bottom, 2mm cavity depth, and some 40mm to clamp the sample holder to a bench) and print some dozens of them using identical g-code. mark the sample holders with the concentration and acid used on the holder part. Next is adding one drop of each tested acid to each sample holder and have it sit there for 24 hours.
Trish
CC BY-SA 4.0
2019-04-11T21:41:46.580Z
You could do accelerated testing by putting PLA in hot HCL solution.  It might have a chance with HCL.  It wouldn't have much chance with HNO3 or H2SO4.  Chlorinated plastics are usually stable.  Don't use Clorox, Muriatic acid is HCL.
Perry Webb
CC BY-SA 4.0
2019-04-11T22:50:05.013Z
@LuxClaridge: As Perry noted, Clorox is not HCl. "Muriatic acid" is indeed the easy ordinary-consumer-available source of HCl.
R.. GitHub STOP HELPING ICE
CC BY-SA 4.0
2019-04-12T13:03:55.047Z
Woops, totally blanked there. It was The Works toilet bowl cleaner that I was what I should have said.
Lux Claridge
CC BY-SA 4.0
2019-04-13T00:34:26.700Z
Interesting question. Web research only led to anecdotes that PLA is not terribly resistant to HCL but I couldn't find anything definitive. PLA is a polyester, so data on polyester may give some guidance. https://www.engineeringtoolbox.com/chemical-resistance-polyester-d_784.html This report is on other plastics, but it gives good background on chemical resistance and factors that affect it such as temperature and mechanical stress. https://plasticpipe.org/pdf/tr-19_thermoplastic_pipe_for_transport_of_chemical.pdf
T. M.
CC BY-SA 4.0
2019-04-13T12:46:50.827Z
Found another article: http://www.fastenercomponents.com/news/acid-resistant-pla/ That lists the best acid resistant plastics. None that I've searched so far are 3D printable. Also found more material that indicated PLA is likely to be less acid resistant than polyester (usually that means PET if not specified) I think this is one of those cases where 3D printing isn't the right solution. Hot high concentration acid solutions are the worst, and maybe with cooler low concentration you would be fine. If you do some testing, please update.
T. M.
CC BY-SA 4.0
2019-04-26T20:14:21.700Z
This might be of use, from Chemistry.SE: [How to dissolve PLA (polylactic acid)?](https://chemistry.stackexchange.com/questions/83476/how-to-dissolve-pla-polylactic-acid). Doesn't mention HCl though, unfortunately, but does mention bio-degradability. TBH, you would be better off asking this question on Chemistry.SE, which is a shame as, if you did, you'd have to delete the question on this site, as you can't x-post.
Greenonline
CC BY-SA 4.0
2019-04-26T22:12:43.960Z
@Greenonline: Why is cross-posting not acceptable? Last I checked it was fine as long as the question was separately on-topic for both SE sites, but maybe something has changed or this policy is specific to either 3dp or chem SE?
R.. GitHub STOP HELPING ICE
CC BY-SA 4.0
2019-04-26T22:14:02.147Z
Read [Can I cross post my question from one site to another?](https://meta.stackexchange.com/questions/71938/can-i-cross-post-my-question-from-one-site-to-another) and in particular [Is cross-posting a question on multiple Stack Exchange sites permitted if the question is on-topic for each site?](https://meta.stackexchange.com/questions/64068/is-cross-posting-a-question-on-multiple-stack-exchange-sites-permitted-if-the-qu/64073#64073) and [this answer](https://meta.stackexchange.com/questions/64068#64069). So *no*... would be the answer, 99.9% of the time :-) Do you want me to migrate it?
Greenonline
CC BY-SA 4.0
2019-04-26T22:27:57.523Z
@Greenonline: If you think it would get more relevant eyes on chem SE, please do. It's not getting any here, anyway.
R.. GitHub STOP HELPING ICE
CC BY-SA 4.0
2019-04-26T23:00:23.890Z
To be migrated you should, and I quote: `This should be fine when limited to acids only, otherwise it might be too broad. It would be good to give it a better title and mention what PLA is, too.`
Greenonline
<pla><material>
PLA chemical resistances? Especially HCl, other acids
R.. GitHub STOP HELPING ICE
# PLA chemical resistances? Especially HCl, other acids

(Asked by: username_0 on 2019-04-11)

I'm interested in 3d printed reaction chambers, but can't find any good information on chemical resistances of PLA, just vague claims that it "might not be" "because it's biodegradable" or that it depends on additives (likely true, but it would be nice to know if there's hope of finding PLA without problematic additives if the PLA itself is okay). Is there any published research or even anecdotes (which could suggest it's worth spending effort to investigate further) on this topic?

**Tags:** pla, material
> **Comments:**
> **username_1**: You could test HCl resistance by squirting out some clorox into a small glass and dip a failed print in. Other acids may be hard to come by using common household chemicals.  
> **username_2**: actually, this calls for a lab test... I would suggest to design some kind of sample piece (like, a small tray with a diameter 2mm cylindrical cavity, 1.5mm material to the sides, 1mm bottom, 2mm cavity depth, and some 40mm to clamp the sample holder to a bench) and print some dozens of them using identical g-code. mark the sample holders with the concentration and acid used on the holder part. Next is adding one drop of each tested acid to each sample holder and have it sit there for 24 hours.  
> **username_3**: You could do accelerated testing by putting PLA in hot HCL solution.  It might have a chance with HCL.  It wouldn't have much chance with HNO3 or H2SO4.  Chlorinated plastics are usually stable.  Don't use Clorox, Muriatic acid is HCL.  
> **username_0**: @LuxClaridge: As Perry noted, Clorox is not HCl. "Muriatic acid" is indeed the easy ordinary-consumer-available source of HCl.  
> **username_1**: Woops, totally blanked there. It was The Works toilet bowl cleaner that I was what I should have said.  
> **username_4**: Interesting question. Web research only led to anecdotes that PLA is not terribly resistant to HCL but I couldn't find anything definitive. PLA is a polyester, so data on polyester may give some guidance. https://www.engineeringtoolbox.com/chemical-resistance-polyester-d_784.html This report is on other plastics, but it gives good background on chemical resistance and factors that affect it such as temperature and mechanical stress. https://plasticpipe.org/pdf/tr-19_thermoplastic_pipe_for_transport_of_chemical.pdf  
> **username_4**: Found another article: http://www.fastenercomponents.com/news/acid-resistant-pla/ That lists the best acid resistant plastics. None that I've searched so far are 3D printable. Also found more material that indicated PLA is likely to be less acid resistant than polyester (usually that means PET if not specified) I think this is one of those cases where 3D printing isn't the right solution. Hot high concentration acid solutions are the worst, and maybe with cooler low concentration you would be fine. If you do some testing, please update.  
> **username_5**: This might be of use, from Chemistry.SE: [How to dissolve PLA (polylactic acid)?](https://chemistry.stackexchange.com/questions/83476/how-to-dissolve-pla-polylactic-acid). Doesn't mention HCl though, unfortunately, but does mention bio-degradability. TBH, you would be better off asking this question on Chemistry.SE, which is a shame as, if you did, you'd have to delete the question on this site, as you can't x-post.  
> **username_0**: @Greenonline: Why is cross-posting not acceptable? Last I checked it was fine as long as the question was separately on-topic for both SE sites, but maybe something has changed or this policy is specific to either 3dp or chem SE?  
> **username_5**: Read [Can I cross post my question from one site to another?](https://meta.stackexchange.com/questions/71938/can-i-cross-post-my-question-from-one-site-to-another) and in particular [Is cross-posting a question on multiple Stack Exchange sites permitted if the question is on-topic for each site?](https://meta.stackexchange.com/questions/64068/is-cross-posting-a-question-on-multiple-stack-exchange-sites-permitted-if-the-qu/64073#64073) and [this answer](https://meta.stackexchange.com/questions/64068#64069). So *no*... would be the answer, 99.9% of the time :-) Do you want me to migrate it?  
> **username_0**: @Greenonline: If you think it would get more relevant eyes on chem SE, please do. It's not getting any here, anyway.  
> **username_5**: To be migrated you should, and I quote: `This should be fine when limited to acids only, otherwise it might be too broad. It would be good to give it a better title and mention what PLA is, too.`  

---

## 3 answers

### Answer by username_0 on 2020-06-17. Score: 2 | Accepted answer

The paper [Chemical Compatibility of Fused Filament Fabrication-based 3-D Printed Components with Solutions Commonly Used in Semiconductor Wet Processing](https://www.researchgate.net/publication/326697946_Chemical_Compatibility_of_Fused_Filament_Fabrication-based_3-D_Printed_Components_with_Solutions_Commonly_Used_in_Semiconductor_Wet_Processing), found by user R Kiselev in the comments on [another question](https://3dprinting.stackexchange.com/questions/13897/how-to-get-a-quality-print-of-a-thin-single-walled-shell), has results for this, and finds (this is summarized; details in paper) that PLA has fairly good resistance to HCl at 37%. It did not fare as well against other acids or solvents except IPA.


---

### Answer by username_6 on 2019-07-22. Score: 3

As @T. M. notes in his comment, there are many good charts of chemical compatibility with various agents. Very few (I found none) include information about PLA. By all means, use search engines to find some information.

But, no data source is as true to your specific needs as is testing your candidate materials with your agents.

As a first test put the agent in a tall thin jar or test tube. Use a few test filaments so that the ends are dipping into the agent. Check for signs of dissolution, swelling, softening, or any relevant change in the material's characteristics. Examine the candidate filaments right away, then after minutes, then hours, and if any material survives, perhaps in days.

Print test objects. Test them with your agent. Try until you find something that works.

The online material compatibility tables will help you eliminate materials before testing them. If it says a material is incompatible, it probably is incompatible. If rated as highly compatible, it should be tested because the formulation of a filament may not match the material tested for the compatibility tables. If you are running out of options, try the intermediate compatibility plastics.

Bottom line, use the online information to help direct your search, but you should do your own tests.


---

### Answer by username_7 on 2022-01-19. Score: 2

See this as well:

[Chemical Resistance of 3D Printing Filament](https://www.filamentive.com/chemical-resistance-of-3d-printing-filament/) by Ravi Toor

> Summarised chemical resistance per material below (***H**= High Resistance, **VH** = Very High Resistance*).
>
> **Water** – PLA (H) PETg (VH), CF-PETg (VH), ASA (VH), ABS (VH), ePLA (H), ONE PET (H)
>
> **Acids** – PETg (VH), ASA (VH), ABS (H)
>
> **Bases**– PETg (VH), CF-PETG (VH), ASA (VH)
>
> **Alcohols** –PETg (H), CF-PETG (VH), ASA (VH), ABS (H)
>
> **Hydrocarbons** – N/A
>
> **Ketones** –N/A
>
> **Ethers** –N/A
>
> **Fuels** –PETg (H), CF-PETG (H)
>
> **Salts** – PLA (H), ASA (VH), ABS (VH), ePLA (H)
>
> **UV** –PLA (H), ASA (VH), ABS (H), ePLA (H)
>
> **Oils** – PLA (H), PETg (VH), CF-PETg (VH), ASA (H), ePLA (H)

> **Comments:**
> **username_8**: Welcome to 3D Printing SE and thank you for your contribution. When you get a chance, please take the [tour] to understand how the site works and how it is different than others.  

---